Engineering Plastic Liner Plate for Mine Hoist / Guide Pulley

• Customization: Available
• Material: GM-3
• Kind: Engineering Plastic Sheet
• Model NO.: many specifications
• Water Absorption: ＜0.01%
• Tensile Strength: 19.1MPa
• Name: Mine Hoist Liner
• Bending Strength: 26.22 MPa
• Thermal Decomposition Temperature: 320 Degree
• Breaking Elongation: 10.6%
• Transport Package: by Container with Plastic Anti-Corrosion Material
• Specification: many specifications
• Trademark: citichl
• Origin: China
• HS Code: 4016991000
• Production Capacity: 1000000 Pieces

Product Description

            Engineering plastic liner plate for mine hoist / guide pulley
Information about mine hoist liner: 
Friction Liner is one of the main components of multi- rope friction hoist, which are PVC and CPUR previously. Friction coefficient of PVC is low (0.28). CPUR has better abrasion resistance than PVC, however, its friction coefficient is 0.20~0.23 and difficult to be machined, has unstable quality due to process reason and found melted in service course, so CPUR is only used with friction coefficient of 0.20~0.23. All the friction Liner with more than 0.25 friction coefficient used in home - made multi - rope hoist needs to be imported overseas, which is very expensive and the import duration time is very long.
GM - 3 high performance friction liner researched and developed from 1997 has met above requirement and passed the provincial technical appraisal on Sep. 12th, 2001.
 
Technical Characteristics:
1. All the friction coefficients of GM - 3 in various conditions are more than 0.25, even more than 0.28 tested by China Mining University and Luoyang Mining Machinery Engineering Design and Research Institute, which completely fulfills the requirements of multi - rope friction hoist.
2. High mechanical strength, thermal resistance and melting resistance better than imported liner, no material damaging steel wire rope, being easy to machine groove in worksite.
3. Be better matched with friction fat whether which is home-made or imported. Ailisi 400 is the beat friction fat.
4. Price is more competitive than imported liner, and brings Customer better economic benefit.
5. Test results show its thermal resistance, melting resistance and abrasion resistance are better than imported liner, and the abrasion per power is equivalent to imported liner.
 

Mechanical Properties

No.	Item	Unit	Results	Remarks
1	Density	g/cm3	1.36
2	Hardness	HD	70-74	GB/T2411
3	Impact Strength	KJ/M2	9.72	GB1843
4	Tensile Strength	Mpa	19.10	GB1040
5	Bending Strength	Mpa	26.22	GB9341
6	Bending Modulus	Mpa	920	GB9341
7	Breaking Elongation	%	10.6	GB1040
8	Compression Strength	Mpa	45.6	GB1040
9	Thermal Decomposition Temperature	ºC	320

 
Difference of abrasion Per Power Tested of GM-3 and K25

Sample No.		Weight Before Test (g)	Weight After Test (g)	abrasion (g)	Total abrasion (g)	Volume (cm3)	abrasion Per Power (10-6cm3/KN·m)
K25	1″	549.70	549.23	0.47	0.75	0.481	5.29
	2″	548.12	547.84	0.28
GM-3	1″	513.44	513.15	0.29	0.56	0.412	5.29
	2″	523.22	522.95	0.27